OILES 470-02/02W Carbon fiber composite bearing for underwater use

STANDARD PRODUCT CUSTOMIZED PRODUCT

Submergible sophisticated bearing with wear resistance
Split metal for flocculator (Customized product) 47H Flocculator bearing unit(Customized product) UPF
OILES 470 is a bearing obtained by compression molding reinforced mixture of carbon fiber or cotton added with a special solid lubricant. Features Self-lubricating capability with low coefficient of friction and high resistance to wear especially in cases of underwater, in-chemical liquid and in-oil application Retainable of stable performance with excellent wear resistance even under abrasive circumstances where soil, sand or other foreign matters are encountered or the mating material is forming rust Available of multiplayer type (470-02W) consisting of 470-02 for sliding surface and 250 or 425 for packing material Standard products of split metals and bearing units for flocculator available upon order
Service Range Lub state underwater Service temperature range -40~+90 P max. N/mm2{ kgf/cm2} 15{ 153} V max. m/s{ m/min} 16.5{ 990} PV max. N/mm2·m/s{ kgf/cm2·m/min} 8.15{ 4990} Condition: In the air, Bushing, Shaft Rotation	Mechanical Property Specific gravity JIS K 6911 ---------- 1.4 Tensile strength JIS K 6911 N/mm2{ kgf/mm2} 45{ 4.6} Bending strength JIS K 6911 N/mm2{ kgf/mm2} 75{ 7.7} Compressive strength JIS K 6911 N/mm2{ kgf/mm2} 124{ 12.7} Radial crushing strength JIS Z 2507 N/mm2{ kgf/mm2} 60{ 6.1} (Compressive molding) Hardness JIS K 6911 ---------- HRM103 Izod impact strength (with-notch) JIS K 6911 J/m{ kgf-cm/cm} 58.8{ 6} Coefficient of linear expansion ASTM D 696 ×10-5-1 2~2.5 Swelling rate ------ % 1.0 (Room temperature) * Values above are nominal values, not standard values.
Test data
Highspeed underwater journal rotating test <Test conditions> Mating material: SUS403 Load: 1.96N/mm2{20kgf/cm2} Velocity: 5m/s {300m/min} Testing time: 8h Lubrication: Fresh water