OILES Glitron F Fluoroethylene resin bearing with filler

STANDARD PRODUCT HALF FINISHED PRODUCT CUSTOMIZED PRODUCT

Excellent resistance to chemical attack and corrosion. Usable for wide range of temperature
Standard Product INDEX OILES Glitron F Bushing 77B OILES Glitron F Flange bushing 77F OILES Glitron F Round bar 77M OILES Glitron F Bushing material 77S OILES Glitron F Plate material 77P OILES Glitron F Skiving sheet 77SH
OILES Glitron F is a self-lubricating bearing based on fluoroethylene containing solid lubricant and anti-abrasion filler. Features The complete self-lubricating bearing keeps low coefficient of static friction at starting without stick slip Excellent wear resistance and very low coefficient of friction under high velocity operations Excellent resistance to chemical attack Food sanitation law compliance Wide service revge from low to high temperature Possible to use soft metals (aluminum and others) as mating shaft Easy to machine
Service Range Lub state: Self-lub Service temperature range -200~+200 P max. N/mm2{ kgf/cm2} 7.0{71} V max m/s{ m/min} 1.65{ 99} PV max. N/mm2·m/s{ kgf/cm2·m/min} 1.00{ 612}	Mechanical Property Specific gravity ASTM D 792 ---------- 2.25 Tensile strength ASTM D 638 N/mm2{ kgf/cm2} 13.1{ 134} Tensile break elongation ASTM D 638 % 150 Compressive stress 1% deformation Compressive stress 10% deformation ASTM D 695 N/mm2{ kgf/cm2} 10.5 { 107} 23.0 { 235} Hardness ASTM D 785 ---------- HRR25 Coefficient of linear expansion ASTM D 696 ×10-5-1 9~11 Melting point DSC 327 Bulk-resistance ASTM D 257 m { ·cm} 3.04{ 3.04×102} Surface resistivity ASTM D 257 8.35×102 * Values above are nominal values, not standard values. (Note 1) Hardness: HDD-typeD durometer hardness
Test data
Journal rotating test <Test conditions> Dimensions of specimen: 10×14×L10 Mating material: SUS303 (Surface roughness 1.2 mRy) Load: 1.96N/mm2{20kgf/cm2} Velocity: 0.500m/s {30m/min} Testing time: 100h Lubrication Self-lub