Standard product which provides electric conductivity with various sizes ponding to miniature bearings.
|
Standard Material INDE
| OILES Glitron SE Bushing |
GEB |
 |
| OILES Glitron SE Flange bushing |
GEF |
|
OILES Glitron SE Bushing
(As a substitute for miniature bearing) |
GSB |
|
OILES Glitron SE Flange bushing
(As a substitute for miniature bearing) |
GSF |
|
|
 |
OILES Glitron SE is a derivative from OILES Glitron S mixed with a special additive dispersed to provide electric conductivity while its sliding characteristics maintained intact.
|
| Features |
 |
Applicable in completely self-lub state. Stable friction characteristics due to small difference between static and dynamic coefficient of friction |
|
Broad service range from low to high temperature |
|
Capable to use soft metals including aluminum as a mating sh |
|
Superb dimensional stability facilitating high precision design allowing mass production by injection molding |
|
Providing electroconductivity of charging with electricity prevention level |
|
Available of standard products with various sizes corresponding to miniatures bearings |
|
|
| Service Range |
| Lub state |
Self-lub
|
| Service temperature range |
-60~+200
|
P max.
N/mm2{ kgf/cm2} |
14.5{ 148}
|
V max.
m/s{ m/min} |
2.50{ 150}
|
PV max.
N/mm2mm/s{ kgf/cm2·m/min} |
0.65{ 398}
|
|
| Mechanical Property |
| Specific gravity |
ASTM D 792
|
----------
|
1.6
|
| Tensile strength |
ASTM D 638
|
N/mm2{ kgf/cm2}
|
41.3{ 421.1} |
| Tensile break elongation |
ASTM D 638
|
%
|
0.99
|
| Bending strength |
ASTM D 790
|
N/mm2{ kgf/cm2}
|
62.9{ 641.6}
|
| Bending elastic modulus |
ASTM D 790
|
N/mm2{ kgf/cm2}
|
3430{ 35000}
|
| Compressive stress 5% deformation |
ASTM D 695
|
N/mm2{ kgf/cm2}
|
72.4{ 739}
|
| Hardness |
ASTM D 785
|
----------
|
HRR116
|
Izod impact strength
(with-notch) |
ASTM D 256
|
J/m{ kgfcm/cm}
|
15.2{ 1.55}
|
| Coefficient of linear expansion |
ASTM D 696
|
×10-5 -1
|
7 |
| Melting point |
DSC
|
|
281
|
| Bulk-resistance |
ASTM D 257 |
 m{·cm} |
2.4×102{ 2.4×104} |
| UL flame resistance |
UL94
|
----------
|
V-0
|
| * Values above are central values, not standard values. |
|
|
| Test data |
| Journal rotating test |
| <Test conditions> |
| Dimensions of specimen: |
 10×14×L10 |
| Mating material: |
SUS440 (Surface roughness 0.2a) |
| Load: |
0.245N/mm2 {2.5kgf/cm2} |
| Velocity: |
1.049m/s {62.8m/min} |
| Atmosphere temperature |
Room temperature |
| Testing time: |
60h |
| Lubrication: |
Self-lub |
|
 |
|