OILES Lutech GP
Polyacetal resin bearing with filler
CUSTOMIZED
PRODUCT

Free from abnormal noise at sliding movement against plastic material
photo
OILES Lutech GP is composed of plyacetal resin added with various lubricant and fillers for better sliding movement in case the mating material is made from plastic
Features ballUsable without lubrication
ballAvailable to use plastic as mating material
ballLow friction coefficient under various loads
ballFree from abnormal noise at sliding movement against plastic material
ballOutstanding wear resistance
ballInjection molding enables complex shape. Suitable for mass production
Service Range
Mating material Plastic Metal
Lub state
Self-lub
Service temperature range
-40~+80
P max.
N/mm2{ kgf/cm2}
3.92
{ 40}
 9.81
{ 100}
V max.
m/s{ m/min}
0.33
{ 20}
 0.67
{ 40}
PV max.
N/mm2·m/s{ kgf/cm2·m/min}
0.163
{ 100}
 0.327
{ 200}
Mechanical Property
Specific gravity
ASTM D 792
----------
1.35
Tensile strength
ASTM D 638
N/mm2{ kgf/cm2}
48.0{ 490}
Tensile break elongation
ASTM D 638
%
40
Bending strength
ASTM D 790
N/mm2{ kgf/cm2}
64.8{ 661}
Bending elastic modulus
ASTM D 790
N/mm2{ kgf/cm2}
2006{ 20471}
Hardness
ASTM D 785
----------
HRM65
Izod impact strength
(with-notch)
ASTM D 256
J/m{ kgfcm/cm}
36.8{ 3.75}
UL flame resistance UL94 File No. E78113 HB
* Values above are nominal values, not standard values.
Test data
Journal rotating test
<Test conditions>
Dimensions of specimen: fai10×fai14×L10
Mating material: POM
Load: 0.07N/mm2{0.72kgf/cm2}
Velocity: 0.15m/s {9.0m/min}
Environmental temperature: 23c
Testing time 950h
Lubrication: Self-lub
Wear amount 0.018m
graph
Products | Bearing Top