OILES 500SP1 High-strength brass base/ Plugged solid lubricants bearing

STANDARD PRODUCT CUSTOMIZED PRODUCT

Metal bearing with wide range of technical achievements
Standard Product INDEX OILES 500SP Bushing (Internal diameter6~45) SPB OILES 500SP Bushing (Internal diameter50~200) SPB OILES 500SP SL-4 bushing SPBL OILES 500SP Flange bushing SPF OILES 500SP Thrust and Journal bushing SPFG OILES 500SP Thrust washer SPW OILES 500SP Flange guide bushing SGF OILES 500SP Guide bushing SGB OILES 500SP Guide Post MGP OILES 500SP Ware plate, General purpose type SWP OILES 500SP Flat plate material SFP OILES 500SP Plate, Type L SLP OILES 500SP Slide Core Guide Rail SLC OILES 500SP Slide Core Guide Rail for Additional Machining SLI
OILES 500 SP1 is a self-lubricating bearing for heavy load applications. It consists of a high strength brass alloy base, prepared through an advanced casting technique in which for self-lubricating feature a proprietary solid lubricant buried therein. Features Exhibits incomparable performance under a high load, low speed operation. Usable without lubrication Excellent wear resistance in such places where an oil film is difficult to be formed due to reciprocating, oscillating motions and frequently intermittent operations Remarkable resistance to corrosion and resistance to chemical attack Available in various dimensions standard products
Service Range for #500SP1-SL1 Lube state No external lube Periodical lub Service temperature range -40~+300 -40~+150 P max. N/mm2{ kgf/cm2} 29(150) { 296(1,530)} V max. m/s{ m/min} 0.50{ 30} 1.00{ 60} PV max. N/mm2·m/s{ kgf/cm2·m/min} 1.65{ 1010} 3.25{ 1990} Service Range for #500SP1-SL4 Lube state No external lube Service temperature range -40 ～ +80 P max. N/mm2{ kgf/cm2} 49(150) { 500(1,530)} V max. m/s{ m/min} 0.25{ 15} PV max. N/mm2·m/s{ kgf/cm2·m/min} 1.65{ 1010} Values in ( ) are of static allowable pressure. Indicates static allowable pressure either without sliding or when sliding with extremely low velocity less than 0.0017m/s {0.1m/min}.	Mechanical Property Density ---------- g/cm3 7.8 Tensile strength JIS Z 2241 N/mm2{ kgf/mm2} 755{ 77} Tensile elongation at break JIS Z 2241 % 12 Compressive strength ---------- N/mm2{ kgf/mm2} 345{ 35} (Note 1) Impact strength JIS Z 2242 J/cm2{ kgfm/cm2} 19{ 1.9} Hardness JIS Z 2243 ---------- HB210 Modulus of longitudinal elasticity JIS Z 2241 N/mm2{ kgf/mm2} 105,000{ 10,700} Coefficient of linear expansion ---------- ×10-5-1 2.2 Thermal conductivity ---------- W/m{cal/seccm} 87.8{ 0.21} * Values above are central values, not standard values. ((Note 1) Compressive proof stress: 0.1%
Test data
Journal rotating test (#500SP1-SL1) <Test condition> Bearing dimension: 40×50×L30 Mating material: S45C High-frequency quenching Pressure: 24.5N/mm2 {250kgf/cm2} Velocity: 0.033m/s {2.0m/min} Testing time: 100h Test environment: Room temperature in the air Lubrication: Self-lube
Journal oscillation test (#500SP1-SL4) <Test condition> Bearing dimension: 40×50×L30 Mating material: SUS304 Pressure: 29.4N/mm2 {300kgf/cm2} Velocity: 0.012m/s {0.75m/min} Oscillating cycle: 12cpm Oscillating angle: ±45° No. of oscillation: 70,000cycle(97.2h) Atmosphere: in the atomosphere Lubrication: SL464 grease is initially applied.
Underwater journal oscillation test (#500SP1-SL4) <Test condition> Bearing dimension: 60×75×L50 Mating material: SUS403 Pressure: 24.5N/mm2 {250kgf/cm2} Velocity: 0.018m/s {1.13m/min} Oscillating cycle: 12cpm Oscillating angle: ±45° No. of oscillation: 70,000cycle(97.2h) Atmosphere: in freshwater Lubrication: SL464 grease is initially applied.
Products | Bearing Top