Oiles 81 Oil-impregnated polyolefin bearings Feature Serviceable without the need for lubrication. Features low coefficient of friction and superior impact resistance performance. Demonstrates superior wear resistance in abrasive conditions due to foreign matter, coarse surfaces of mating parts, rust, etc. Injection-molded and can be made in complicated shapes. Has good mass productivity. Specific gravity Tensile strength Tensile elongation at break Flexural property Flexural modulus Hardness Izod impact strength (with notch) Co-efficient of linear expansion Deflection temperature under load 0.45 MPa Melting point UL incombustibility ASTM D 792 ASTM D 638 ASTM D 638 ASTM D 790 ASTM D 790 ASTM D 785 ASTM D 256 ASTM D 696 ASTM D 648 DSC UL94 Mechanical properties 81-12 81-20 Compressive stress 1% deformation 10% deformation 1.00 26.5o270p 200 22.5o230p 980o10,000p HRR35 147o15.0p 11`13 . 137 . 0.97 32.4o330p 10 33.3o340p 1,550o15,800p HRR60 98.1o10.0p 11`13 85 130iNote 1j HB 8.3o85p 26.5o270p 10.8o110p 26.5o270p ASTM D 695 The values shown above are typical values, not the standard values. iNote 1jvalues by vicat softening point (ASTM D 1525) Service range Lubrication condition Service temperature range Allowable max. pressure P N/mmo2 kgf/cm2p Allowable max. velocity V m/som/minp Allowable max. PV value N/mm2Em/sokgf/cm2Em/minp |60`{60 5.0o51p 0.25o15p 0.80o489p |60`{60 3.0o31p 0.50o30p 0.80o489p Dry 81-12 81-20 . N/mmo2 kgf/cm2p N/mmo2 kgf/cm2p N/mmo2 kgf/cm2p N/mmo2 kgf/cm2p . J/mokgfcm/cmp ~10|5 |1 File No.E78113 i81-12j 91Selection Guide Product Air Bearings Metallic Bearing Multi-layer Bearing Plastic Bearing Information Technical Corporate Profi le Information Slide Shifter